China Electrical Insulation Board

≥33kJ/m2 Charpy Impact Strength Electric Insulation Material With High Compressive Strength Of ≥350MPa

Color:Yellow

Tensile strength(MD):≥300MPa

Flexural strength perpendicular to laminations(MD):≥340MPa
Electrical Insulation Board Electrical Insulation With Our Superior Insulation Board

Electric strength perpendicular to laminations(at 90℃±2℃ in oil), 1mm in thickness:≥14.2kV/mm

Shape:Board

Temp. Index:120℃
Electrical Insulation Board With High Electric Strength And Low Relative Permittivity

Tensile strength(MD):≥300MPa

Size:102 X 202cm

Density:≥1.8g/cm3
Tensile Strength MD ≥300MPa Electric Insulation Material With Phenolic Epoxy Resin Glass Fiber

Color:Yellow

Tensile strength(MD):≥300MPa

Flexural strength perpendicular to laminations(MD):≥340MPa
Yellow Electrical Insulation Board With Relative Permittivity 50Hz ≤5.5 And Breakdown Voltage Parallet To Laminations At 90C±2C In Oil ≥35kV

Size:102 X 202cm

Shape:Board

Compressive strength:≥350MPa
Density Electrical Insulation Board Relative Permittivity 50Hz ≤5.5 Density≥1.8g/cm3

Breakdown voltage parallet to laminations(at 90℃±2℃ in oil):≥35kV

Color:Yellow

Surface:Smooth/no Significant Defect
Plate / Sheet Electric Insulation Material With Epoxy Resin / Fiberglass Cloth Composition

Water Absorption:≤0.04%

Vertical BDV:≥11.8kv/mm In Oil Of 90℃

Size:1220x2040/1020x1220
Epoxy Resin / Fiberglass Cloth Electrical Insulation Board High Insulation Efficiency

Vertical compression strength:≥350MPa

Size:1220x2040/1020x1220

Vertical BDV:≥11.8kv/mm In Oil Of 90℃
Smooth Electrical Insulation Board Plate / Sheet Density 1.8 - 2.0g/Cm3 Flexural Strength ≥340MPa

Water Absorption:≤0.04%

Dielectric Constant:≤5.5

Density:1.8-2.0g/cm3
0.2mm - 30mm Thickness Electrical Insulation Board Vertical Compression Strength ≥350MPa

Vertical compression strength:≥350MPa

Dielectric Constant:≤5.5

Thickness:0.2mm-30mm
0.2mm - 30mm Thickness Electrical Insulation Board Vertical Compression Strength 350MPa

Vertical compression strength:≥350MPa

Vertical BDV:≥11.8kv/mm In Oil Of 90℃

Thickness:0.2mm-30mm
0.2mm - 30mm Electrical Insulation Board Good Electrical Stability And High Mechanical Strength

Vertical compression strength:≥350MPa

Thickness:0.2mm-30mm

Material:Epoxy Resin/Fiberglass Cloth

Page 3 of 4|< << 1 2 3 4 >> >|

Electrical Insulation Board

Electrical board With Smooth Surface 0.1mm - 100mm Thickness superior insulation

China Electrical Insulation Board

≥33kJ/m2 Charpy Impact Strength Electric Insulation Material With High Compressive Strength Of ≥350MPa

Electrical Insulation Board Electrical Insulation With Our Superior Insulation Board

Electrical Insulation Board With High Electric Strength And Low Relative Permittivity

Tensile Strength MD ≥300MPa Electric Insulation Material With Phenolic Epoxy Resin Glass Fiber

Yellow Electrical Insulation Board With Relative Permittivity 50Hz ≤5.5 And Breakdown Voltage Parallet To Laminations At 90C±2C In Oil ≥35kV

Density Electrical Insulation Board Relative Permittivity 50Hz ≤5.5 Density≥1.8g/cm3

Plate / Sheet Electric Insulation Material With Epoxy Resin / Fiberglass Cloth Composition

Epoxy Resin / Fiberglass Cloth Electrical Insulation Board High Insulation Efficiency

Smooth Electrical Insulation Board Plate / Sheet Density 1.8 - 2.0g/Cm3 Flexural Strength ≥340MPa

0.2mm - 30mm Thickness Electrical Insulation Board Vertical Compression Strength ≥350MPa

0.2mm - 30mm Thickness Electrical Insulation Board Vertical Compression Strength 350MPa

0.2mm - 30mm Electrical Insulation Board Good Electrical Stability And High Mechanical Strength

Adhesive Insulation Tape

0.10mm Acrylic Aramid Paper Adhesive Tape 10mm-980mm

PI Film Adhesive Insulation Tape F Grade Electrial Insulation

3mm-500mm Waterproof Electrical Insulation Tape Amber Transparent

Glass Cloth Insulation Tape

0.08-0.25mm Glass Tape For Insulation Aluminum Glass Cloth Tape

0.13mm White Temperature Resistant Fiberglass Cloth Insulation Tape

Ivory Color Electrical Silicone Fiberglass Insulation Casing With 0.5~25mm O.D.